Accelerating the decarbonization of carbonaceous gold ore by suspension oxidation roasting towards the improvement of gold leaching efficiency

Eliminating the gold preg-robbing effect of carbonaceous matter in carbonaceous gold ores is crucial for gold leaching. In this study, suspension oxidation roasting was proposed to accelerate the decarbonization of carbonaceous gold ore. The characteristics of oxidation reaction process and gas release were analyzed by TG-DTA-FTIR. The phase transformation and microstructure evolution of samples during roasting were analyzed by XRD, SEM and BET. The results show that the gold preg-robbing effect was eliminated after the gasification of carbonaceous matter, and the CaO generated by decomposition of carbonates can effectively capture the SO₂. After roasting for 75 min at 650 °C in a 20% O₂ atmosphere, the total carbon removal rate reached 99.42%, the distribution of exposed gold increased from 28.85% to 77.10% and the gold leaching efficiency increased from 4.55% to 84.83%. In addition, about 70% sulfur was mainly fixed in the roasted products in the form of sulfate. Therefore, the suspension oxidation roasting process is an efficient and clean pretreatment method for carbonaceous gold ores.     

井下硐室大爆破实践

酒钢镜铁山矿运用硐室大爆破处理山头岩体，以便为２号（中）矿体的开采形成良好的覆盖层。由于爆破设计合理，工程质量较好，达到了预期的目的。     

Ceramics composites from iron ore tailings and blast furnace slag

The search for materials and methods capable of reducing human impacts on the environment is of utmost importance nowadays. This study's primary purpose was to analyze the technical feasibility of ceramic composites production utilizing Fundão Dam's Iron Ore Tailings (IOT), Blast Furnace Slag (BFS) from charcoal, and Foundry Sand (FS) as partial substitutes for the traditional raw materials – sand and clay – for application in building industry materials. The composites were molded in rectangular specimens and fired at temperatures of 900, 950, 1000, 1050, and 1200 °C. The developed materials were analyzed and characterized by X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Energy Dispersive Spectroscopy (EDS), Thermogravimetry (TGA), and Differential Thermal Analysis (DTA). The obtained materials had flexural strength modulus of up to 12.19 MPa, water absorption ranging from 2 to 22%, linear shrinkage ranging from 0.02 to 6.50%, and apparent density ranging from 2.03 to 1.63 g/cm³. The study of the internal structure formation process revealed the formation of amorphous structures in the composites. The results demonstrated that these waste materials may be jointly used in construction materials, contributing to the reduction of natural resource extraction, besides enabling their correct disposal, minimizing environmental impacts, and improving the life quality of the surrounding communities.     

Degradation mechanism of high alumina refractory bricks by reaction with deposits in a rotary kiln for fluxed iron ore pellets production

The formed deposits wear out of refractory wall linings in the rotary kiln and may cause production disturbances. This study describes the chemical composition and mineralogical phase components at the deposit/refractory interface in the rotary kiln for fluxed iron ore pellets production. The main phases of refractory bricks are corundum and mullite, while the deposits mainly contain hematite and silicates. The main phases in the deposit/refractory brick contact zone are hematite, anorthite (CaAl₂Si₂O₈), mullite, corundum, and silicates. Moreover, the hematite phases in the deposit/brick interface averagely contain 6.98 wt% Al and 1.38 wt% Ti. The silicates in the contact zone contain higher aluminium content and lower iron content than the silicates in the deposits. Finally, the thermodynamic analysis indicates that the main phases in the deposits can react with the refractory to form Al₂Fe₂O₆, CaAl₂Si₂O₈, feldspar, and liquid phases lead to the degradation of bricks in the kiln during the iron ore pellets production.     

退火温度对HA/Ti-24Nb-4Zr复合材料组织与性能的影响

利用放电等离子烧结(SPS)技术制备了HA/Ti-24Nb-4Zr生物复合材料,研究了不同退火温度对复合材料显微组织和力学性能(抗压强度、屈服强度、屈强比、压缩弹性模量)的影响。结果表明,烧结态复合材料主要由β-Ti相、少量初生α-Ti相及HA相组成;随着退火温度的升高,复合材料基体中β-Ti相含量增多且晶粒逐渐长大,针状次生α-Ti相在晶界处和晶内不断析出,HA相结构和含量变化不大;与烧结态相比,不同退火温度处理后的复合材料强度和弹性模量先略微上升后下降,而塑韧性呈不断提高趋势;复合材料在850 ℃退火处理后,抗压强度、屈服强度、屈强比和压缩弹性模量值分别为1507 MPa、1270 MPa、0.84和42 GPa,塑韧性得到明显改善,作为生物医用植入材料具有潜在的应用前景。     

Characterisation of the microplasma spraying of biocompatible coating of titanium

This paper presents new results of studying the influence of parameters of microplasma spraying (MPS) of Ti wire on the structure and properties of Ti coatings. Based on the design of the experiment and the results of the SEM study, certain spraying modes were chosen to form the desired composition and structure of the Ti coating.  The dense sublayer (up to 300 µm thick) provides good adhesion to the substrate, and a porous top layer can accelerate the coated implant ingrowth with the bone.  This technology is developed for the manufacture of coated endoprosthesis implants.     

安徽省铜陵市铁山头铜矿床地质特征及找矿潜力

铁山头铜矿床处于铜陵矿集区的中东部，属于扬子陆块下扬子凹陷中的铜陵隆起。矿床位于凤凰山矿田北侧，成矿潜力较大。综合研究分析认为：①接触交代作用使得岩体接触带及附近变质形成矽卡岩矿化带；②区内凤凰山岩体（花岗闪长岩）系成矿母岩；③矿体主要赋存于花岗闪长岩与三叠系下统南陵湖组石灰岩接触带上；④矿床成因类型为高—中温热液交代矽卡岩型矿床。     

臭氧氧化-循环喷淋法处理钨钼选矿废水

采用臭氧氧化-循环喷淋法去除钨钼选矿废水中COD,研究了pH值、臭氧流量、循环频率对COD去除效果的影响。结果表明: 废水COD去除率随pH值、臭氧流量、循环频率增大而增加,在pH值为10、臭氧流量3.0 L/min、循环频率4.0次/min条件下,氧化120 min后废水COD含量由131 mg/L降至11.5 mg/L,COD去除率达91.2%,满足《污水综合排放标准》(GB 8978-1996)一级标准。与O₂、NaClO处理废水COD的对比试验结果表明,循环喷淋法结合O₃表现出较好的COD去除效果。